S235B

2023-05-17 18:53:20 来源：钢铁之家阅读量：0

牌号	S235B
对应标准	ISO 683-18-2014 热处理钢、合金钢和易切削钢 -- 第18部分：光面钢制品 Bright steel products
归类	合金钢

S235B 化学元素成分含量(%)

	成分	C	Mn	P	S ^①	Cu ^③	N ^②
t≤40mm	最小值	-	-	-	-	-	-
t≤40mm	最大值	0.17	1.4	0.04	0.04	0.55	0.012

	成分	C	Mn	P	S ^①	Cu ^③	N ^②
40mm＜t≤100mm	最小值	-	-	-	-	-	-
40mm＜t≤100mm	最大值	0.2	1.4	0.04	0.04	0.55	0.012

① For long products. the max. S content may be increased for improved machinablility ba 0,005 % by agreement if the steel is treated to modify the sulphide morphology and if the chemical composition shows min 0,0020 % Ca.
② The maximum value for nitrogen does not apply if the chemical composition shows a minimum total Al content of 0,020 % or, alternalively, minimum 0,015 % acid soluble Al or if s ufficient other N-binding elements are present. In this case, the N-binding elements shall be mentioned in the inspection document.
③ Cu contenl above 0,40 % can cause hot shortness during hot forming.

碳当量计算

S235B 机械性能

厚度 t mm	热处理或状态	抗拉强度 σ_b Mpa	屈服点 σ_s Mpa	断后伸长率或延伸率 δ %	硬度 HBW
5≤t≤10	Cold drawn (+C)	470~840	≥355	≥8
10＜t≤16	Cold drawn (+C)	420~770	≥300	≥9
16＜t≤40	Cold drawn (+C)	390~730	≥260	≥10
40＜t≤63	Cold drawn (+C)	380~670	≥235	≥11
63＜t≤100	Cold drawn (+C)	360~640	≥215	≥11
16＜t≤100	As-rolled + peeled (+SH)	360~510			107~152

近似对照表碳素结构钢和工程用钢

中国	国际标准组织	欧标
GB	ISO	EN	数字牌号
Q235B	S235B	S235JRC	1.0122

注：本资料来源于互联网的公开资源整理，我们不保证这些资料的准确性、完整性和适用性。这些资料仅供您参考，不应用于任何商业用途或决策依据。本资料所记载的技术信息是说明产品的代表性特点和性能的参考值，对于因误用或不当使用本资料所记载的信息等而造成的损害恕难承担责任，敬请周知。