2205 HS

2023-05-17 18:04:43 来源：钢铁之家阅读量：0

牌号	2205 HS
美国UNS	S32205 HS
对应标准	ASTM A313/A313M-2018 不锈钢弹簧丝 Stainless Steel Spring Wire
归类	双相不锈钢
标签	奥氏体-铁素体
说明	“HS”高强度本标准适用于制造弹簧的奥氏体、奥氏体-铁素体、沉淀硬化不锈钢圆钢丝。

2205 HS 化学元素成分含量(%)

成分	C	Si	Mn	P	S	Cr	Ni	Mo	N
最小值	-	-	-	-	-	22	4.5	3	0.14
最大值	0.03	1	2	0.03	0.02	23	6.5	3.5	0.2

碳当量计算

2205 HS 机械性能

直径 d mm	抗拉强度 σ_b Mpa
0.2≤d≤0.7	2370~2730
0.7＜d≤0.8	2230~2570
0.8＜d≤1	2140~2460
1＜d≤1.5	2090~2410
1.5＜d≤2	2000~2300
2＜d≤2.5	1910~2190
2.5＜d≤3	1860~2140
3＜d≤3.5	1810~2090
3.5＜d≤4	1770~2030
4＜d≤4.5	1720~1980
4.5＜d≤5	1670~1930

注：Tensile requirements for high strength cold drawn, as-delivered wire. Tensile strength can be increased by 29 ksi [200 MPa] up to 65 ksi [450 MPa] by tempering depending on tensile and tempering conditions. Recommendations: 840°F [450℃]/1~3 h for batch tempering; 950°F [500°C] for 3 to 10 minutes in a continuous conveyor furnace. Shorter times may result in uneven tempering.
During storage, the tensile strength will increase somewhat due to aging. Depending on the storage conditions, the tensile strength can Increase by 0~12ksi [0~80 MPa].