牌号	A2
对应标准	BS 3100-1991 一般工程用铸钢件 Specification for Steel castings for general engineering purposes
归类	铸钢
标签	碳钢铸钢

A2 化学元素成分含量(%)

成分	C	Si	Mn	P	S
最小值	-	-	-	-	-
最大值	0.35	0.6	1	0.05	0.05

①碳含量每降低0.01%，最大锰含量则增加0.04%，允许最大锰含量到1.1%

碳当量计算

A2 机械性能

热处理或状态	抗拉强度 σ_b Mpa	屈服点 σ_s Mpa	断后伸长率或延伸率 δ %	冲击吸收能量 KV2 J
A或N或N+T或OQ+T或WQ+T	≥490	≥260	≥18	≥20

A=for anneal by heating to a temperature above the AC3 and cool in the furnace
N=for normalize by heating to a temperature above the AC3 and cool in still air
OQ=for quench into oil from a temperature above the AC3
WQ=for quench into water from a temperature above the AC3
AH=for air harden by heating to a temperature above the AC3 and cool in air at a rate fast enough to produce a hardened microstructure
T=for temper by heating to a temperature below AC1
ST=for solution treat by heating to temperature high enough to dissolve and any intermetallic phases followed by a rapid cool.

①表中值适用于铸件截面厚度小于等于500mm，超过此尺寸的机械性能应与制造商协商。
②如果买方要求对此牌号进行冲击试验，则不进行弯曲试验

近似对照表铸钢

中国	日本	美国	国际标准组织	德国		俄罗斯	英国
GB	JIS	UNS	ISO	DIN EN/DIN	W-Nr.	GOST	BS EN/BS
ZG270-500	SC480	J04000	270-480	GS-60 GS-62	1.0553 1.0555	35Л	A2