GX25CrNiSi20-14

2023-05-17 18:46:37 来源：钢铁之家阅读量：0

牌号	GX25CrNiSi20-14
德国W-Nr.	1.4832
对应标准	DIN 17465-1993 耐热铸钢 Heat resisting steel castings - Technical delivery conditions
归类	铸钢
标签	奥氏体型耐热铸钢最高工作温度950°C

GX25CrNiSi20-14 化学元素成分含量(%)

成分	C	Si	Mn	P	S	Cr	Ni
最小值	0.15	1	-	-	-	19	13
最大值	0.3	2.5	1.5	0.035	0.03	21	15

碳当量计算

GX25CrNiSi20-14 机械性能

产品	热处理或状态	抗拉强度 σ_b Mpa	屈服点 σ_s Mpa	断后伸长率或延伸率 δ %	硬度 HBW
铸钢	铸态	≥440①	≥230	≥10①	-

①适用于厚度t≤25mm的产品

Material		Den- sity, in g/cm³	Thermal con- ductivity, in W/K.m	Specific heat capacity at 20 °C, in J/g.K	Coefficient of linear thermal expansion, in 10^-6 /K, at a temperature between 20 °C and
designation	number	Den- sity, in g/cm³	Thermal con- ductivity, in W/K.m	Specific heat capacity at 20 °C, in J/g.K	400 °C	800°C	1000°c
GX25CrNiSi20-14	1.4832	7.8	14.6	0.50	17.5	18.5	19.5

Material

suitable fillet metal

Heat treatment

designation

number

Covered electrode (symbol)

Wire or rod
(symbol)

Material number

prior to welding

after welding

GX25CrNiSi20-14

1.4832

22 12

25 20hC*

X12CrNi22-12 X40CrNi25-21

1.4829

1.4846

不预热或只稍微预热(到摸起来温暖)。

不需热处理

*hC表示高含碳量

近似对照表耐热铸钢和耐热合金铸件

注：本资料来源于互联网的公开资源整理，我们不保证这些资料的准确性、完整性和适用性。这些资料仅供您参考，不应用于任何商业用途或决策依据。本资料所记载的技术信息是说明产品的代表性特点和性能的参考值，对于因误用或不当使用本资料所记载的信息等而造成的损害恕难承担责任，敬请周知。

上一篇：ZG20Mn
下一篇：GX40CrSi23

Material		1% creep limit after 10000 h, in N/mm², at a temperature, in °C, of						Maximum service temperature, in °C
designation	number	600	700	800	900	1000	1100	Maximum service temperature, in °C
GX25CrNiSi20-14	1.4832	82	46	23	10	-	-	950